| Product Name | MOPLEN PP HP456J |
| Manufacturer | LyondellBasell |
| Polymer Type | Polypropylene Homopolymer |
| Form | Pellets |
| Melt Flow Rate | 14 g/10min (230°C/2.16kg) |
| Density | 0.905 g/cm³ |
| Tensile Modulus | 1600 MPa |
| Tensile Strength | 35 MPa |
| Elongation At Break | 12% |
| Vicat Softening Point | 150°C |
| Applications | Injection molding |
| Color | Natural |
| Processing Temperature | 200-260°C |
| Moisture Absorption | <0.02% |
As an accredited MOPLEN PP HP456J factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The packaging for **MOPLEN PP HP456J** typically features a 25 kg white plastic bag, labeled with product name and manufacturer details. |
| Storage | **MOPLEN PP HP456J** should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and moisture. Keep it in original, tightly closed packaging to prevent contamination. Avoid exposure to strong oxidants and sources of ignition. Ensure proper labeling and stack to prevent bags from collapsing or damage. Follow local regulations for polypropylene storage. |
| Shipping | **Shipping Description for MOPLEN PP HP456J:** MOPLEN PP HP456J is shipped as polypropylene resin in pellet form. It should be transported in moisture-proof, sealed bags, typically 25 kg each, and protected from direct sunlight, heat, and moisture. Handle according to standard industrial hygiene, and ensure compliance with local and international transport regulations. |
Competitive MOPLEN PP HP456J prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615371019725 or mail to sales7@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615371019725
Email: sales7@ascent-chem.com
Wusu, Tacheng Prefecture, Xinjiang, China