| Product Name | ExxonMobil PP1304E5 |
| Material Type | Polypropylene Homopolymer |
| Melt Flow Rate 230c 2 16kg | 13 g/10min |
| Density | 0.905 g/cm3 |
| Tensile Strength At Yield | 37 MPa |
| Elongation At Yield | 10% |
| Flexural Modulus | 1700 MPa |
| Izod Notched Impact 23c | 35 J/m |
| Heat Deflection Temperature 0 45mpa | 110°C |
| Ash Content | ≤0.03% |
| Maximum Usage Temperature | 100°C |
| Typical Applications | Injection molding, housewares, containers |
As an accredited ExxonMobil PP1304E5 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The **ExxonMobil PP1304E5** is typically packaged in 25 kg white plastic bags, featuring product labeling, batch number, and ExxonMobil branding. |
| Shipping | ExxonMobil PP1304E5 is typically shipped in 25 kg bags or 1,000 kg bulk bags (FIBCs), securely palletized and shrink-wrapped for stability and protection. Shipments comply with relevant safety and handling regulations, and require storage in cool, dry areas away from direct sunlight, chemicals, or sources of ignition to maintain product integrity. |
| Storage | ExxonMobil PP1304E5 should be stored in a cool, dry, well-ventilated area, away from direct sunlight, heat, and sources of ignition. The product should be kept in original, unopened packaging to prevent contamination and moisture absorption. Avoid exposure to strong oxidizing agents and extreme temperatures to maintain material integrity and performance. Handle in accordance with standard polymer storage guidelines. |
Competitive ExxonMobil PP1304E5 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!