| Product Name | Borouge PP BF970MO |
| Polymer Type | Polypropylene Random Copolymer |
| Melt Flow Rate 230c 2 16kg | 70 g/10min |
| Density | 0.90 g/cm3 |
| Tensile Modulus | 1100 MPa |
| Tensile Strength At Yield | 28 MPa |
| Elongation At Yield | 10% |
| Flexural Modulus | 950 MPa |
| Izod Notched Impact Strength 23c | 4.0 kJ/m2 |
| Heat Deflection Temperature 0 45mpa | 104°C |
| Haze Thickness 1mm | 11% |
| Application | Injection Molding |
As an accredited Borouge PP BF970MO factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The packaging for Borouge PP BF970MO consists of 25 kg white plastic bags, labeled with product name, grade, and manufacturer details. |
| Storage | Borouge PP BF970MO should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and moisture. The packaging should remain sealed and undamaged to prevent contamination. Avoid exposure to strong oxidizing agents. Proper pallet stacking and handling are recommended to maintain the material’s quality and prevent deformation. Store according to local regulations for polyolefin materials. |
| Shipping | Borouge PP BF970MO is shipped in standard 25 kg bags, securely sealed to prevent contamination and moisture absorption. Bags are packed on pallets, typically wrapped for additional protection during transportation. Ensure storage in a cool, dry place, away from direct sunlight. Handle in compliance with local regulations for polyolefin materials. |
Competitive Borouge PP BF970MO prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615371019725 or mail to sales7@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615371019725
Email: sales7@ascent-chem.com
Wusu, Tacheng Prefecture, Xinjiang, China