| Material Name | Laser+ GP (S92XR) |
| Polymer Type | Polyethylene terephthalate (PET) |
| Form | Pellets |
| Melt Flow Index | 16 g/10 min (at 265°C/2.16kg) |
| Density | 1.36 g/cm³ |
| Intrinsic Viscosity | 0.72 dL/g |
| Glass Transition Temperature | 75°C |
| Melting Point | 255°C |
| Tensile Strength | 50 MPa |
| Elongation At Break | 120% |
| Flexural Modulus | 2100 MPa |
| Clarity | High |
| Moisture Absorption | 0.5% (24 hr, 23°C) |
| Application | General Purpose, Laser Marking |
As an accredited Laser+ GP (S92XR) Polyethylene terephthalate (PET) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Laser+ GP (S92XR) Polyethylene terephthalate (PET) is packaged in 25 kg multilayer kraft paper bags with inner polyethylene lining. |
| Storage | Laser+ GP (S92XR) Polyethylene terephthalate (PET) should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat or ignition. Keep the material in its original packaging, sealed tightly to prevent contamination and moisture absorption. Avoid stacking heavy materials on top to prevent deformation, and ensure the storage area is free of strong oxidizing agents. |
| Shipping | Laser+ GP (S92XR) Polyethylene terephthalate (PET) is shipped in standard, tightly sealed, moisture-proof packaging, typically as pellets in 25 kg bags or bulk containers. Shipments are protected from direct sunlight, contaminants, and physical damage. Proper handling ensures material integrity and compliance with safety regulations during transport and storage. |
Competitive Laser+ GP (S92XR) Polyethylene terephthalate (PET) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales2@boxa-chem.com