HS Code |
643021 |
| Product Name | Lupoy GP-1000ML |
| Material Type | Polycarbonate (PC) |
| Manufacturer | LG Chem |
| Melt Flow Index | 10 g/10 min (300°C/1.2kg) |
| Density | 1.2 g/cm³ |
| Tensile Strength | 60 MPa |
| Flexural Modulus | 2350 MPa |
| Heat Deflection Temperature | 135°C (at 1.8 MPa) |
| Transparency | High |
| Flame Retardancy | UL94 HB |
| Moisture Absorption | 0.15% (24 hrs, 23°C) |
As an accredited Lupoy GP-1000ML Polycarbonate (PC) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Lupoy GP-1000ML Polycarbonate (PC) is packaged in a 25 kg white plastic bag with blue and red branding and labeling. |
| Storage | Lupoy GP-1000ML Polycarbonate (PC) should be stored in a cool, dry, well-ventilated area, away from direct sunlight, moisture, and sources of heat or ignition. Keep the material in its original, tightly sealed packaging to prevent contamination and degradation. Avoid storage near strong acids or bases. Proper storage preserves material quality and extends shelf life, ensuring optimal performance in processing and applications. |
| Shipping | Lupoy GP-1000ML Polycarbonate (PC) is shipped in secure, moisture-resistant packaging, typically 25 kg bags or drums, to prevent contamination and damage during transit. Packages are clearly labeled with safety and handling instructions. Storage and transport should avoid direct sunlight, high temperatures, and moisture to maintain product quality. |
Competitive Lupoy GP-1000ML Polycarbonate (PC) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
West Ujimqin Banner, Xilingol League, Inner Mongolia, China