| Manufacturer | LG Chem |
| Product Name | Lupoy 1303AH-15 |
| Polymer Type | Polycarbonate (PC) |
| Melt Flow Index Mfi | 13 g/10 min (300°C, 1.2 kg) |
| Density | 1.2 g/cm³ |
| Tensile Strength | 62 MPa |
| Flexural Modulus | 2,300 MPa |
| Impact Strength Izod Notched | 65 J/m |
| Heat Deflection Temperature Hdt | 132°C (at 1.8 MPa) |
| Light Transmittance | 89% |
| Vicat Softening Point | 147°C |
| Flame Rating | UL94 V-2 |
As an accredited Lupoy 1303AH-15 Polycarbonate (PC) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Lupoy 1303AH-15 Polycarbonate (PC) is packaged in 25 kg polyethylene bags, featuring the Lupoy logo, product name, and handling instructions. |
| Shipping | Lupoy 1303AH-15 Polycarbonate (PC) is shipped in moisture-resistant, sealed bags or containers, typically 25 kg each, to protect against contamination and moisture absorption. Packages should be handled with care, stored in a cool, dry place, and transported according to relevant safety regulations, avoiding exposure to direct sunlight and physical damage. |
| Storage | Lupoy 1303AH-15 Polycarbonate (PC) should be stored in a cool, dry, well-ventilated area away from direct sunlight and sources of heat or ignition. Keep the material in its original, tightly sealed packaging to prevent moisture absorption and contamination. Avoid storage near strong oxidizing agents or chemicals. Ensure that handling equipment and storage facilities minimize the risk of dust development and physical damage. |
Competitive Lupoy 1303AH-15 Polycarbonate (PC) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!