HS Code |
980240 |
| Product Name | Lupoy 1201-22 Polycarbonate (PC) |
| Manufacturer | LG Chem |
| Material Type | Polycarbonate |
| Melt Flow Index | 22 g/10min (at 300°C, 1.2kg) |
| Density | 1.2 g/cm³ |
| Tensile Strength | 60 MPa |
| Flexural Modulus | 2,400 MPa |
| Vicat Softening Temperature | 146°C |
| Molding Temperature | 260–300°C |
| Glass Transition Temperature | 148°C |
As an accredited Lupoy 1201-22 Polycarbonate (PC) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Lupoy 1201-22 Polycarbonate (PC) is typically packaged in 25 kg white polyethylene bags labeled with product name, manufacturer, and batch details. |
| Storage | Lupoy 1201-22 Polycarbonate (PC) should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat. Keep the resin in tightly sealed original packaging to prevent moisture absorption. Avoid contamination with dust or other materials. Storage temperatures should ideally be below 30°C to maintain product quality and processing characteristics. |
| Shipping | Lupoy 1201-22 Polycarbonate (PC) is shipped in moisture-resistant, multi-layered bags or containers, typically weighing 25 kg each. Packaging ensures protection from contaminants and environmental factors. Pallets are used for bulk orders, and all shipments are clearly labeled with product identification, safety information, and manufacturer details to comply with transportation regulations. |
Competitive Lupoy 1201-22 Polycarbonate (PC) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
West Ujimqin Banner, Xilingol League, Inner Mongolia, China