| Product Name | CLARNATE FC3105 Polycarbonate |
| Material Type | Polycarbonate (PC) |
| Melt Flow Index | 11 g/10 min (at 300°C/1.2 kg) |
| Density | 1.20 g/cm³ |
| Tensile Strength | 62 MPa |
| Flexural Modulus | 2,300 MPa |
| Vicat Softening Point | 145°C |
| Glass Transition Temperature | 148°C |
| Mold Shrinkage | 0.5 – 0.7% |
| Light Transmittance | 89% |
| Flammability Rating | UL94 V-2 |
As an accredited CLARNATE FC3105 Polycarbonate (PC) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | CLARNATE FC3105 Polycarbonate (PC) is packaged in 25 kg white polyethylene bags, displaying product name, grade, and handling instructions. |
| Storage | CLARNATE FC3105 Polycarbonate (PC) should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat. The material must remain in its original, tightly sealed packaging to prevent moisture absorption and contamination. Avoid exposure to harsh chemicals, as this could affect its properties. Proper storage ensures optimal performance and extends shelf life. |
| Shipping | CLARNATE FC3105 Polycarbonate (PC) is typically shipped in secure, moisture-resistant packaging such as 25 kg bags or bulk containers. During transit, it is protected from direct sunlight, moisture, and physical damage. Handling requires appropriate labeling and adherence to standard safety guidelines for thermoplastic resins to ensure safe delivery. |
Competitive CLARNATE FC3105 Polycarbonate (PC) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
West Ujimqin Banner, Xilingol League, Inner Mongolia, China