| Product Name | CLARNATE A1030 |
| Polymer Type | Polycarbonate (PC) |
| Melt Flow Rate 300c 1 2kg | 10 g/10min |
| Tensile Strength | 62 MPa |
| Flexural Strength | 95 MPa |
| Flexural Modulus | 2300 MPa |
| Izod Impact Strength Notched 23c | 62 J/m |
| Rockwell Hardness | R118 |
| Glass Transition Temperature | 150°C |
| Light Transmittance | 89% |
| Density | 1.2 g/cm³ |
| Vicat Softening Point | 146°C |
As an accredited CLARNATE A1030 Polycarbonate (PC) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | CLARNATE A1030 Polycarbonate (PC) is typically packaged in 25kg white polyethylene bags with clear labeling and manufacturer details. |
| Storage | CLARNATE A1030 Polycarbonate (PC) should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, moisture, and sources of ignition. Keep the material in tightly sealed original containers or packaging to prevent contamination and hydrolysis. Avoid exposure to extreme temperatures, and ensure the storage area is clean and free from incompatible chemicals, such as strong acids and bases. |
| Shipping | CLARNATE A1030 Polycarbonate (PC) is shipped in moisture-resistant, sealed kraft paper bags or bulk containers, typically weighing 25 kg per bag. Ensure storage in a cool, dry place, away from direct sunlight and contaminants. During transit, protect from excessive heat, humidity, and physical damage to maintain material integrity. |
Competitive CLARNATE A1030 Polycarbonate (PC) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales9@bouling-chem.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@bouling-chem.com
West Ujimqin Banner, Xilingol League, Inner Mongolia, China