902812 |
| Brand | Ultramid |
| Grade | PA66 A3HG7 |
| Polymer Type | Polyamide 66 (Nylon 66) |
| Reinforcement | 35% Glass Fiber |
| Color | Natural (can be colored) |
| Density | 1.41 g/cm³ |
| Tensile Strength | 180 MPa |
| Flexural Modulus | 9000 MPa |
| Notched Izod Impact Strength | 9 kJ/m² |
| Melting Point | 260°C |
| Mold Shrinkage | 0.2 - 0.5 % |
| Water Absorption 24h | 0.35 % |
| Flammability | UL 94 HB |
| Heat Deflection Temperature 1 8 Mpa | 250°C |
| Electrical Volume Resistivity | 1.0 x 10^12 Ω·cm |
As an accredited Ultramid PA66 A3HG7 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The Ultramid PA66 A3HG7 is packaged in a 25 kg blue BASF-branded polyethylene bag, with clear product labeling and safety instructions. |
| Shipping | Shipping of Ultramid PA66 A3HG7, a polyamide 66 (nylon) resin, requires sealed, moisture-proof packaging, typically in 25 kg bags or bulk containers. Store and transport under dry conditions away from direct sunlight and extreme temperatures. Ensure compliance with local regulations and safety data sheets for secure handling and transportation. |
| Storage | Ultramid PA66 A3HG7 should be stored in its original, tightly sealed containers in a cool, dry place, protected from direct sunlight and moisture. Avoid exposing the material to extreme temperatures to maintain quality. Keep away from sources of ignition and incompatible substances. Proper storage conditions help preserve the material’s mechanical and processing properties for optimal performance. |
Competitive Ultramid PA66 A3HG7 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!