| Product Name | Celstran PA66-GF60-02 |
| Base Polymer | Polyamide 66 (Nylon 66) |
| Glass Fiber Content | 60% |
| Color | Natural |
| Density | 1.68 g/cm³ |
| Tensile Modulus | 17000 MPa |
| Tensile Strength | 255 MPa |
| Elongation At Break | 2.3% |
| Flexural Modulus | 15000 MPa |
| Melt Flow Rate | 30 g/10min (275°C/5kg) |
| Heat Deflection Temperature | 250°C (1.8 MPa) |
| Water Absorption 24h | 0.7% |
| Flammability Rating | HB (UL 94) |
| Processing Method | Injection Molding |
As an accredited Celstran PA66-GF60-02 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Celstran PA66-GF60-02 is packaged in 25 kg moisture-resistant bags, clearly labeled with product name, batch, and safety instructions. |
| Shipping | **Shipping Description for Celstran PA66-GF60-02:** Celstran PA66-GF60-02 is shipped as reinforced polyamide granules in sealed, moisture-protected bags or containers. Each package is properly labeled, securely palletized, and transported under dry, ambient conditions to prevent contamination or moisture uptake. Handle with care to avoid package damage during transit and storage. |
| Storage | Celstran PA66-GF60-02 should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat. Keep the material in its original, tightly sealed packaging to prevent moisture absorption. Avoid exposure to strong oxidizing agents. Proper storage helps maintain the product’s quality and processability before use in manufacturing applications. |
Competitive Celstran PA66-GF60-02 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!