| Product Name | Novamid PA6 1010N2 1ES NAT |
| Polymer Base | Polyamide 6 (PA6) |
| Form | Pellets |
| Color | Natural (uncolored) |
| Melt Flow Rate 275c 5kg | 2.6 g/10 min |
| Density | 1.13 g/cm³ |
| Tensile Strength Yield | 85 MPa |
| Elongation At Break | 50% |
| Flexural Modulus | 3000 MPa |
| Notched Izod Impact 23c | 6 kJ/m² |
| Water Absorption 24h | 1.4% |
| Molding Temperature | 240-280°C |
| Vicat Softening Temperature | 215°C |
| Applications | Injection molding |
As an accredited Novamid PA6 1010N2 1ES NAT factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Novamid PA6 1010N2 1ES NAT is typically packaged in 25 kg (55 lbs) moisture-proof, polyethylene-lined paper bags for protection. |
| Shipping | Novamid PA6 1010N2 1ES NAT is shipped in 25 kg moisture-protected bags or bulk containers, clearly labeled for identification and traceability. Packaging ensures safe, secure transport, protecting material integrity from dust and moisture. Store in a cool, dry place and avoid direct sunlight to maintain product quality during shipping and storage. |
| Storage | Novamid PA6 1010N2 1ES NAT should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of moisture. Keep the material in its tightly sealed original packaging to prevent contamination and water absorption. Avoid exposure to temperatures above 50°C. Handle according to standard polymer safety guidelines, and ensure good housekeeping to prevent unnecessary dust accumulation. |
Competitive Novamid PA6 1010N2 1ES NAT prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!