| Material Type | High Density Polyethylene (HDPE) |
| Grade | CRP 100 BLACK |
| Color | Black |
| Density | 0.950 g/cm³ |
| Melt Flow Rate | 10 g/10 min (190°C/5kg) |
| Tensile Modulus | 1000 MPa |
| Tensile Strength At Yield | 25 MPa |
| Elongation At Break | >600% |
| Charpy Notched Impact Strength | 25 kJ/m² |
| Thermal Conductivity | 0.5 W/(m·K) |
| Vicat Softening Temperature | 126°C |
| Application | Pressure Pipes |
| Uv Stabilization | Yes |
| Carbon Black Content | 2.0-2.5% |
| Standard Compliance | ISO 4427 / EN 1555 |
As an accredited Hostalen HDPE CRP 100 BLACK factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Hostalen HDPE CRP 100 BLACK is typically supplied in 25 kg white plastic bags, labeled with product name, grade, and manufacturer. |
| Shipping | Hostalen HDPE CRP 100 BLACK is typically shipped in 25 kg polyethylene bags, palletized and shrink-wrapped for protection. Ensure storage in a dry, ventilated area away from direct sunlight and sources of heat. Follow safety guidelines for handling, and refer to the Safety Data Sheet (SDS) for further shipping and transport instructions. |
| Storage | Hostalen HDPE CRP 100 BLACK should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat. The material should be kept in its original packaging and protected from moisture and contamination. Avoid exposure to strong oxidizing agents. Proper storage ensures the maintenance of its quality and technical properties over time. |
Competitive Hostalen HDPE CRP 100 BLACK prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615380400285 or mail to sales2@boxa-chem.com.
We will respond to you as soon as possible.
Tel: +8615380400285
Email: sales2@boxa-chem.com
Flexible payment, competitive price, premium service - Inquire now!