| Product Name | Novodur ABS H802 |
| Manufacturer | INEOS Styrolution |
| Polymer Type | Acrylonitrile Butadiene Styrene (ABS) |
| Grade | High Impact Injection Molding |
| Density | 1.04 g/cm3 |
| Melt Flow Rate | 5.5 g/10min (220°C/10kg) |
| Tensile Strength | 44 MPa |
| Elongation At Break | 40% |
| Flexural Modulus | 2200 MPa |
| Impact Strength Notched Izod | 18 kJ/m2 (23°C) |
| Vicat Softening Temperature | 96°C |
| Processing Temperature | 220 - 260°C |
As an accredited Novodur ABS H802 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Novodur ABS H802 is typically packaged in 25 kg multi-layered, moisture-resistant polyethylene bags displaying the manufacturer's branding and product information. |
| Storage | Novodur ABS H802 should be stored in its original, tightly sealed packaging in a cool, dry, and well-ventilated area. Avoid exposure to direct sunlight, heat, and moisture to prevent material degradation. Keep away from incompatible substances and sources of ignition. Proper storage ensures the product retains its quality and extends its shelf life for optimal processing performance. |
| Shipping | Novodur ABS H802 is shipped in standard, sealed 25 kg bags or bulk containers to prevent contamination and moisture absorption. Packaging is secure and labeled according to international transport regulations for chemicals. During transport, the material should be kept dry and protected from direct sunlight, excessive heat, and physical damage. |
Competitive Novodur ABS H802 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615371019725 or mail to sales7@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615371019725
Email: sales7@ascent-chem.com
Wusu, Tacheng Prefecture, Xinjiang, China